CN102350136A - Ceramic filter element and preparing method thereof - Google Patents
Ceramic filter element and preparing method thereof Download PDFInfo
- Publication number
- CN102350136A CN102350136A CN2011102637858A CN201110263785A CN102350136A CN 102350136 A CN102350136 A CN 102350136A CN 2011102637858 A CN2011102637858 A CN 2011102637858A CN 201110263785 A CN201110263785 A CN 201110263785A CN 102350136 A CN102350136 A CN 102350136A
- Authority
- CN
- China
- Prior art keywords
- filter element
- ceramic element
- ceramic filter
- parts
- preparing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramic filter element and a preparing method thereof. The ceramic filter element is prepared according to the following steps: mixing and stirring raw materials in part by weight, wherein the raw materials contain kieselguhr, kaolin, wood powder, adhesive CMC (Carboxy Methylated Cellulose), water, carbon dust, straw ash, phenolic resin, magnesium oxide and natural zeolite; and then performing casting forming or compacting forming on a mixture; and drying and then roasting at 900-1300 DEG C, thereby acquiring the ceramic filter element. The preparing method is simple, the prescription is reasonable, the cost is low, and the prepared ceramic filter element is excellent in heat resistance and abrasive resistance.
Description
Technical field
The present invention relates to a kind of ceramic element and preparation method thereof, belong to the cleaner field.
Background technology
As everyone knows; The filter opening of traditional ceramic element is all superfine little; And be high density and distribute; Therefore for the higher area of water turbidity; As easy as rolling off a log round mud or iron rust etc. block than coarse granule impurity; Filter the water yield and influence it; So the low-density ceramic filter core that has big filter opening together or together all is set in the front of this high density ceramic filter core usually again; Utilize preposition ceramic element to remove thicker thick impurity in the water in advance; Mud; Suspended material etc.; So as to protecting rearmounted activated carbon ceramic element; High density ceramic filter cores such as ion exchange resin ceramic element or pellicle (R0) ceramic element make the thick impurity lining of thicker of its unlikely quilt and influence function such as the clean or absorption of its filter.Its major defect is: preposition ceramic element commonly used; It is nothing more than being to be made up of materials such as PP plastic cement, fiber, knitting wool; So after blocking, promptly must abandon; Can't wash once more for repeated use, not only expendable is big for it, causes the manpower and materials burden; And owing to do not meet environmental protection condition; Can't accomplish decomposition at short notice, so that all become environment high pollution material, not meet economic environmental requirement in the future.
Summary of the invention
Deficiency and defective in order to solve prior art the object of the present invention is to provide a kind of ceramic element and preparation method thereof.Preparation method of the present invention is simple, and prescription is reasonable, and cost is low, and the ceramic element that makes is heat-resisting, wearability good.
The present invention adopts following technical scheme to achieve these goals:
Ceramic element is characterized in that the weight portion of its constitutive material is: diatomite 35-40 part, kaolin 10-15 part, wood powder 6-9 part, adhesive C MC 6-8 part, water 40-50 part, carbon dust 10-15 part, stalk ashes 3-5 part, phenolic resins 20-30 part, magnesia 10-15 part and natural zeolite 10-15 part are arranged.
The preparation method of described ceramic element is characterized in that: the weight portion by constitutive material takes by weighing each constitutive material, mixes and stirs after injection forming or pressed compact moulding 900-1300 ℃ of calcining, promptly get this ceramic element after the drying.
Beneficial effect of the present invention:
Preparation method of the present invention is simple, and prescription is reasonable, and cost is low, and the ceramic element that makes is heat-resisting, wearability good.
The specific embodiment
Embodiment 1:Ceramic element, the weight portion of its constitutive material is: 10 parts of 35 parts in diatomite, 10 parts of kaolin, 6 parts of wood powders, 6 parts of adhesive C MC, 40 parts in water, 10 parts of carbon dusts, 3 parts in stalk ashes, 20 parts in phenolic resins, 10 parts in magnesia and natural zeolites are arranged.
The preparation method of ceramic element takes by weighing each constitutive material by the weight portion of constitutive material, mixes and stirs after injection forming or pressed compact moulding, and dry back promptly gets this ceramic element 900-1300 ℃ of calcining.
The Static Water adsorbance 17.3% of obtained ceramic element; Compression strength 5012N; Compatibility 0.008%.
Embodiment 2:Ceramic element, the weight portion of its constitutive material is: 12 parts of 37 parts in diatomite, 12 parts of kaolin, 8 parts of wood powders, 7 parts of adhesive C MC, 45 parts in water, 12 parts of carbon dusts, 4 parts in stalk ashes, 25 parts in phenolic resins, 12 parts in magnesia and natural zeolites are arranged.
The preparation method of ceramic element takes by weighing each constitutive material by the weight portion of constitutive material, mixes and stirs after injection forming or pressed compact moulding, and dry back promptly gets this ceramic element 900-1300 ℃ of calcining.
The Static Water adsorbance 17.6% of obtained ceramic element; Compression strength 5132N; Compatibility 0.0078%.
Embodiment 3:Ceramic element, the weight portion of its constitutive material is: 15 parts of 40 parts in diatomite, 15 parts of kaolin, 9 parts of wood powders, 8 parts of adhesive C MC, 50 parts in water, 15 parts of carbon dusts, 5 parts in stalk ashes, 30 parts in phenolic resins, 15 parts in magnesia and natural zeolites are arranged.
The preparation method of ceramic element takes by weighing each constitutive material by the weight portion of constitutive material, mixes and stirs after injection forming or pressed compact moulding, and dry back promptly gets this ceramic element 900-1300 ℃ of calcining.
The Static Water adsorbance 17.8% of obtained ceramic element; Compression strength 5076N; Compatibility 0.0082%.
Claims (2)
1. a ceramic element is characterized in that the weight portion of its constitutive material is: diatomite 35-40 part, kaolin 10-15 part, wood powder 6-9 part, adhesive C MC 6-8 part, water 40-50 part, carbon dust 10-15 part, stalk ashes 3-5 part, phenolic resins 20-30 part, magnesia 10-15 part and natural zeolite 10-15 part are arranged.
2. the preparation method of a ceramic element as claimed in claim 1, it is characterized in that: the weight portion by constitutive material takes by weighing each constitutive material, mixes and stirs after injection forming or pressed compact moulding, and dry back promptly gets this ceramic element 900-1300 ℃ of calcining.